904L Stainless steel strip Price in China ,Manufacturer of 904L Stainless Steel strip

Super austenitic stainless steel 904L (00Cr20Ni25Mo4.5Cu;
UNS: N08904;
EN: 1.4539) is a low carbon, high-alloy austenitic stainless steel with excellent corrosion resistance in dilute sulfuric acid. It is designed for harsh corrosion conditions.
Has the high chromium content and plenty of nickel content, the addition of copper makes it have strong ability to resist acid, especially for chloride clearance corrosion and stress corrosion cracking are highly resistant, not easy to appear, erosion and fracture pitting resistance slightly better than other steel grade, good machinability and weldability, can be used for pressure vessels.

Since the carbon content of 904L is very low (Max. 0.020%), there will be no carbide precipitation during normal heat treatment and welding.
This eliminates the risk of intergranular corrosion that normally occurs after heat treatment and welding.
Due to the high chromium, nickel, molybdenum content and the addition of copper, 904L can be passivated even in reducing environments, such as sulfuric acid and formic acid.
The high nickel content makes it have a low corrosion rate in the active state.
In the concentration range of 0 to 98% pure sulfuric acid, 904L can be used at temperatures up to 40 degrees Celsius.
Its corrosion resistance is very good in pure phosphoric acid in the concentration range of 0~85%.
In industrial phosphoric acid produced by wet process, impurity has a strong effect on corrosion resistance.
Of all the phosphoric acids, 904L has superior corrosion resistance to ordinary stainless steel.
In highly oxidizing nitric acid, 904L has poor corrosion resistance compared to highly alloyed steels without molybdenum.
In hydrochloric acid, the use of 904L is limited to lower concentrations of 1-2%.
It's in this concentration range.
The corrosion resistance of 904L is better than that of conventional stainless steel.
904L steel has high resistance to pitting corrosion.
It also has excellent crevice corrosion resistance in chloride solutions.
The high nickel content of 904L reduces the corrosion rate in pits and crevices.
Ordinary austenitic stainless steels may be sensitive to stress corrosion at temperatures above 60 ° C in a chloride-rich environment, and this sensitivity can be reduced by increasing the nickel content of the stainless steels.
Due to its high nickel content, 904L is highly resistant to stress corrosion cracking in chloride solutions, concentrated hydroxide solutions and hydrogen sulphide-rich environments.

Standard Specification Of 904L strip

Thickness	0.1mm-12mm
Width	1mm-650mm
Length	Since the custom
Surface	2B, 2D, BA, NO.1, NO.4, NO.8, 8K, mirror, checkered, embossed, hair line, sand blast, Brush, etching, etc
Finish	Hot rolled strip (HR), Cold rolled strip (CR), 2B, 2D, BA NO(8), SATIN (Met with Plastic Coated)
Form	strips, Foils, Rolls, Plain strip, Shim strip, Perforated strip, Chequered strip, Strip, Flats, Blank (Circle), Ring (Flange) etc.

904L stainless steel composition content.

Grade		C	Mn	Si	P	S	Cr	Mo	Ni	Cu
904L	Min. Max.	≤0.03	≤2.00	≤1.00	≤0.035	≤0.03	18.0-20.0	3.0-4.0	23.0-25.0	4.0-5.0

Alloy and state :926,
Tensile strength (Rm N/mm2):490
Yield strength (RP0.2N/mm2):216,
Elongation A5% :35.
Density: 8.24 g/cm3

• 

  904L Stainless steel strip

• 

  904L Stainless steel strip

• 

  904L Stainless steel strip

904L Characteristic machining technology

1D -- The surface has discontinuous granular shape, also known as fog surface.
Processing technology: hot rolling + annealing shot peening pickling + cold rolling + annealing pickling.
2D - A slightly silvery white colour.
Processing technology: hot rolling + annealing shot peening pickling + cold rolling + annealing pickling.
2B -- Silver white with better gloss and flatness than a 2D surface.
Processing technology: hot rolling + annealing shot peening pickling + cold rolling + annealing pickling + quenching and tempering rolling.
Ba - Excellent surface gloss, high reflectivity, like a mirror surface.
Processing technology: hot rolling + annealing shot peening pickling + cold rolling + annealing pickling + surface polishing + quenching and tempering rolling.
No.3 -- Good gloss, coarse grain surface.
Processing technology: polishing and tempering rolling for 2D or 2B with 100~120 abrasive materials (JIS R6002).
No.4 -- Good gloss, fine lines on the surface.
Processing process: polishing and tempering rolling for 2D or 2B with 150~180 abrasive materials (JIS R6002).
HL -- Silver grey with hair streaks.
Processing technology: 2D products or 2B products with appropriate granularity of abrasive materials for polishing the surface is a continuous abrasive grain.
MIRRO -- Specular.
Processing technology: 2D products or 2B products with appropriate granularity of the grinding material grinding and polishing to the mirror effect.

Stainless Steel 904L strip Price List					904Lstrip FOB Shanghai Per Unit (USD)
2mm 904L stainless steel strip					$4500.00-$7000.00
ss 904L mirror Stainless Steel strip/ Strip/ strip					$4800.00-$7300.00
904L Stainless Steel strip / Stainless Steel strip 904L					$4500.00-$7000.00
Standard size 4x8 metal sus 904L grade stainless steel checkered strip prices					$4500.00-$7000.00