The 200 series stainless steel was first developed in the United States during World War II as a substitute for the 300 series stainless steel.
At that time, because of the war, nickel as a strategic material was strictly controlled by the countries concerned, and the supply of nickel in the United States was seriously short.
This new series of austenitic stainless steels with manganese instead of nickel was developed in the United States in order to solve the problem of production and supply of stainless steel under the condition of severe nickel shortage.
After the end of World War II, the supply of nickel in the United States gradually improved, so the production of 300 series stainless steel is no longer restricted by raw material constraints, so the 200 series did not get a big development.
Several original participation in the development of 200 series of stainless steel Indians, after returning to India, from India is a relatively rich in manganese resources, nickel resources lack of national conditions, will be developed in the United States 200 series of stainless steel varieties back to India.
The success of the 200 series stainless steel in India is due to the possibility of replacing 304 stainless steel in some specific applications.
Most of the 200 series stainless steels sold in the Chinese market have little control on sulfur and carbon content according to national standards, and use manganese (and nitrogen) to replace part or all of nickel to produce austenitic stainless steels with lower nickel content.
The disadvantage of this series of materials is: below 18% chromium content and low nickel content can not reach balance and form ferrite, for this reason, 200 series of stainless steel chromium content to 13.5% ~ 15%, in some cases down to 13% ~ 14%, its corrosion resistance is not compared with 304 and other similar steels.
In addition, manganese and, in some cases, copper reduce the effect of re-passivation under acidic conditions common in the corrosion sites of deposits and crevasses.
The destruction rate of 200 series steels under these conditions is approximately 10-100 times that of 304 stainless steels.
The residual sulfur and carbon content of these steels is often not controlled during production, and the material cannot be traced to its source, even when it is recycled.
If Cr-Mn steels are not specified, they can become a dangerous scrap mix, resulting in castings containing unexpectedly high levels of manganese.

This is the most cost effective grade of steel. So the 201 Stainless Steel Sheet Price is lower compared to other grades of stainless steels and all metallic products in general. There are different versions of the material with low carbon and high carbon content.  The low carbon version, 201 sheets are very good for welding applications as they have less carbide precipitation and less localized corrosion.

Standard Specification Of 201 Plate

Thickness	4mm-100mm
Width	1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc
Length	2000mm, 2440mm, 3000mm, 5800mm, 6000mm, etc
Surface	2B, 2D, BA, NO.1, NO.4, NO.8, 8K, mirror, checkered, embossed, hair line, sand blast, Brush, etching, etc
Finish	Hot rolled plate (HR), Cold rolled sheet (CR), 2B, 2D, BA NO(8), SATIN (Met with Plastic Coated)
Form	Coils, Foils, Rolls, Plain Sheet, Shim Sheet, Perforated Sheet, Chequered Plate, Strip, Flats, Blank (Circle), Ring (Flange) etc.

201 stainless steel composition content.

Grade		C	Mn	Si	P	S	Cr	Mo	Ni	N
201	Min. Max.	≤0.15	5.5～7.50	≤1.00	≤0.060	≤0.03	16.0～18.0	/	3.5-5.5	≤0.25

Tensile strength :520MPa
Yield strength :275MPa
Elongation :55 to 60%
Elastic modulus :29,000,000 psi is equivalent to: 203000MPa
Hardness requirement (Brinell hardness)
183 n/was (MPa).
Density :.280 LBS /cubic inch(density 7.93g/cm3)

• 

  201 Stainless steel sheet

• 

  201 Stainless steel sheet

• 

  201 Stainless steel sheet

201 Characteristic machining technology

1D -- The surface has discontinuous granular shape, also known as fog surface.
Processing technology: hot rolling + annealing shot peening pickling + cold rolling + annealing pickling.
2D - A slightly silvery white colour.
Processing technology: hot rolling + annealing shot peening pickling + cold rolling + annealing pickling.
2B -- Silver white with better gloss and flatness than a 2D surface.
Processing technology: hot rolling + annealing shot peening pickling + cold rolling + annealing pickling + quenching and tempering rolling.
Ba - Excellent surface gloss, high reflectivity, like a mirror surface.
Processing technology: hot rolling + annealing shot peening pickling + cold rolling + annealing pickling + surface polishing + quenching and tempering rolling.
No.3 -- Good gloss, coarse grain surface.
Processing technology: polishing and tempering rolling for 2D or 2B with 100~120 abrasive materials (JIS R6002).
No.4 -- Good gloss, fine lines on the surface.
Processing process: polishing and tempering rolling for 2D or 2B with 150~180 abrasive materials (JIS R6002).
HL -- Silver grey with hair streaks.
Processing technology: 2D products or 2B products with appropriate granularity of abrasive materials for polishing the surface is a continuous abrasive grain.
MIRRO -- Specular.
Processing technology: 2D products or 2B products with appropriate granularity of the grinding material grinding and polishing to the mirror effect.

Stainless Steel 201 Plate Price List					201Sheet FOB Shanghai Per Unit (USD)
2mm 201 stainless steel plate					$1500.00-$2000.00
ss 201 mirror Stainless Steel Coil/ Strip/ Sheet					$1800.00-$2300.00
201 Stainless Steel Plate / Stainless Steel Sheet 201					$1500.00-$2000.00
Standard size 4x8 metal sus 201 grade stainless steel checkered Sheet prices					$1500.00-$2000.00